为保证飞机设计满足损伤容限性能要求,有必要对其进行剩余强度评估。针对6156-T4铝合金焊接连接薄壁结构进行了R曲线和剩余强度试验,判断了裂纹扩展经过筋条时的裂纹扩展路径,测量了母板和筋条两个方向的裂纹扩展速率,并采用不同的断裂准则和分析方法对单及双跨度多个初始裂纹长度焊接加筋薄板的剩余强度进行了预测。结果表明:裂纹扩展在经过筋条时,同时沿着母板和筋条继续扩展,筋条上的裂纹扩展方向垂直于母板且两个方向的裂纹扩展速率基本相同;采用净截面屈服准则进行剩余强度预测时会低估这种韧性较好的焊接连接薄壁结构的剩余强度;基于SINTAP-FITNET评价体系,以裂纹尖端张开位移(CTOD-δ5)作为裂纹尖端弹塑性表征参量进行剩余强度预测时,预测结果比采用K曲线预测方法精度高。     

冷板流道结构优化及其钎焊技术

针对航天航空领域中集成电子设备出现的热流密度过高所带来的高效散热技术冷板设计问题与结构制造难题,提出了一种流道设计优化与结构钎焊技术。利用Flotherm热仿真分析软件对导流和结构等进行优化,完成了高效率散热结构设计。同时,对设计的窄流道结构带来的焊接质量问题,进行了钎料和焊接压力参数优化。结果表明:与传统S型流道冷板相比,采用片状导流结构和串并联混合结构的冷板热源温度降低了15℃,并将均温性控制在1.2℃以内。采用控制钎料厚度和工装压力的方法,降低了窄筋流道堵塞和焊接变形趋势。     

航天铝合金深腔零件整体成形预制坯优化设计

提出航天铝合金深腔零件整体成形方法,开展预制坯优化设计。对比分析直筒和变径筒两种预制筒坯结构变形规律,数值模拟研究了底部圆角对开口球形件液压成形的影响规律。以直径D=450 mm的球形整体零件为验证对象,进行底部圆角r=60 mm的变径筒形件的液压成形试验验证。结果表明:直筒坯液压成形时,赤道位置发生破裂;变径筒坯液压成形时,当胀形压力为16 MPa即发生贴模;液压成形时,筒端口自适应补料,所以上半球的壁厚分布均匀;随着底部圆角越大,筒底部减薄越小,筒壁厚越均匀;当底部圆角为r=60 mm时,开口球壳赤道位置壁厚减薄最严重,减薄率为11.1%,球底部减薄率为9.8%,开口球壳上半球壁厚差为0.17 mm,下半球壁厚差为0.43 mm。     

不同温度下TC21钛合金等离子表面渗Cr层的摩擦磨损性能

为提高TC21合金的摩擦磨损性能，采用双辉等离子冶金技术在TC21合金表面制备渗Cr改性层，利用扫描电镜(Scanning electron microscope,SEM),能谱仪(Energy dispersive spectromenter,EDS),显微硬度仪和划痕仪等研究了渗Cr层的组织形貌特征、硬度及结合强度，并 在20,300,500 ℃条件下使用摩擦磨损试验机对基体及渗Cr层的摩擦磨损性能进行对比、探究，并分析磨损机理。结果表明：渗Cr层厚度为30μm，均匀致密，与基体结合力至少能承受64 N的垂直载荷；改性层表面硬度超过1 000 HV0.1，约为基体的3倍；TC21合金渗Cr后，不同温度下的减摩性能和耐磨性能均得到提高。在室温下TC21基体磨损机理主要是磨粒磨损、粘着磨损和氧化磨损，而渗Cr层的磨损机理主要是磨粒磨损；500 ℃时基体粘着磨损和氧化磨损程度变得更加严重，渗Cr层磨损机理是剥层磨损和氧化磨损。      

复杂构件RTM整体成型工艺设计与仿真研究

以飞机预冷气引起口为典型构件,对其成型工艺进行探索,选择RTM成型工艺并应用PAM-RTM软件对RTM成型工艺影响参数进行虚拟仿真,确定模具设计的最终参数值.     

Mg-Sc-Y三元合金的微观组织和力学性能

稀土元素作为重要的镁合金强化相元素,其多元添加产生的影响并未得到充分研究。在Mg-Sc二元系的基础上将Y作为第三元加入,制备了Mg-5Sc二元合金及Mg-5Sc-0.5Y,Mg-5Sc-1Y,Mg-5Sc-2Y,Mg-5Sc-3Y,Mg-5Sc-3.5Y(质量分数,%)5种三元合金,并通过光学显微镜(OM)、扫描电子显微镜(SEM)、X射线衍射(XRD)及室温拉伸等试验,研究了Y元素的加入对Mg-Sc二元合金微观组织和力学性能的影响。结果表明:Y元素在合金中的主要存在形式为固溶态,富集于晶界处。随着Y元素含量的提升,合金晶粒度显著减小,屈服强度和硬度大幅提升,Mg-5Sc-3.5Y的屈服强度相比Mg-5Sc提升了约50%。该强度的提升主要是由细晶强化和固溶强化引起的。     

Microstructure,porosity and mechanical properties of selective laser melted AlSi10Mg

Finite element modeling (FEM), microscopy, X-ray computed tomography (CT) and mechanical property tests were used to study the microstructure, porosity and mechanical properties of an AlSi10Mg alloy produced by selective laser melting (SLM). The simulation of the melt pool and thermal history under different energy densities produced an optimized result with an energy density of 44.5 J·mm⁻³. The high cooling rate during the SLM process significantly refined the previous α-Al dendrites. The growth direction of the network-like Al-Si eutectic structure at different orientations confirmed the anisotropic nature of the microstructure. Furthermore, the microhardness, tensile testing and fracture analysis results proved that there were no obvious distinctions in the strength between the transverse and longitudinal directions, and that the ductility was anisotropic, possibly due to the shape and distribution of the pores. The pores measured by X-ray CT at different energy densities confirmed that the sphericity of the pores was inversely related to pores volumes. With optimized processing conditions, the porosity of the selective laser melted sample decreased leading to the improved fabricated fuel system component via SLM.     

含边缘裂纹铝合金厚板的复合材料双面修补研究

采用表面打磨,80℃、接触压固化的方法,利用碳纤维/双马复合材料预固化补片对边缘裂纹的铝合金厚板进行双面胶接修补,测试修补前后的静态和疲劳性能,并结合高低温老化和常温油浸试验考核其耐煤油性。结果表明:修补后平均破坏载荷由94.313 kN增加到143.593 kN,提高了52.25%;疲劳寿命由2 019次循环增加到34 698次循环,提高了16.19倍;临界裂纹长度由13.5 mm增加为27.5 mm;裂纹扩展速率由2.72 mm/1 000循环降低为0.59 mm/1 000循环。在300次循环高低温油浸及180 d的常温油浸试验条件下,燃油对试验件疲劳性能无影响,同时修补试验件对煤油品质无明显影响。     

热处理对FeCo-2V-0.5Cr软磁合金力学与磁学性能的影响

针对FeCo-2V-0.5Cr软磁合金,研究了真空热处理时间对其微观组织结构、力学与磁学性能的影响规律,发现在800℃下热处理时间为2h左右时,合金的抗拉强度和延伸率达到最佳,同时仍保持良好的软磁性能,抗拉强度、延伸率以及矫顽力分别为867.8MPa、10.4%以及2.0Oe。进一步对该合金进行附加磁场下的真空热处理,重点研究了合金的交流损耗与矫顽力随附加磁场方式包括磁场撤除温度与磁场下保温时间的变化规律,发现适当的磁场热处理对合金相关力学性能影响不大,但由于合金中产生了单轴各向异性而使合金矫顽力进一步降至1.6Oe。     

TA15钛合金电子束焊缝形貌及其组织研究

采用不同工艺参数对TA15钛合金进行电子束焊接,通过观察焊缝形貌、测量其形状参数研究了焊接接头形貌的变化规律,并分析了焊接接头组织。结果表明:增大电子束流时,熔深、半熔深熔宽、焊缝宽度都增大,焊缝横截面的形状从"钉形"转变为"钟罩形";增大焊接速度,对焊缝形状影响不大,熔深、半熔深熔宽及焊缝宽度均减小,深宽比先增大后减小;聚焦电流的增大对熔深作用较明显,半熔深熔宽及焊缝宽度变化不大;扫描幅值的增加使焊缝熔深减小,半熔深熔宽增大。靠近母材的热影响区组织与母材组织相近,主要由初生等轴状α相及转变β相组成,并出现针状(α+β);靠近熔合线的组织由α相和针状(α+β)相构成,并出现α'马氏体;熔合区组织由α'组成,熔合线周围柱状晶垂直于焊缝中心生长,并在焊缝中心形成单列或多列的等轴状晶。